Astratto:

Questo studio indaga l'impatto di diversi leganti in resina sulle prestazioni di taglio degli anelli di filo diamantato. I campioni di durezza polimerizzati con resina sono stati preparati utilizzando resina fenolica pura, resina fenolica epossi-modificata, e resina fenolica alchil-modificata aromatica, e la loro durezza Rockwell è stata testata. Le superfici fratturate dei campioni di resina polimerizzata sono state osservate utilizzando la microscopia elettronica a scansione, Rivelando livelli variabili di densità post-polimerizzazione. Furono poi prodotti anelli di filo diamantato per monocristalli taglio del silicio esperimenti.

The experimental results demonstrate that diamond wire loops made with pure phenolic resin, characterized by high cured hardness and good post-curing density, exhibit minimal wire deflection during cutting, shorter cutting times, reduced diamond particle detachment, and enhanced cutting ability.

Current Development Status of Anello di filo diamantato Taglio

With the increase in the size of single crystal silicon and the rising demands for wafer quality and cutting efficiency, free abrasive wire saw cutting can no longer meet production needs, leading to widespread attention on bonded abrasive diamond wire loops.

Types of Bonded Abrasive Diamond Wire Loops

Bonded abrasive diamond wire loops are mainly divided into electroplated diamond wire loops and resin diamond wire loops. Tra questi, resin diamond wire loops (referred to as resin loops) have the advantages of simple manufacturing process, low cost, Alta efficienza, minimal environmental pollution, and good surface quality of processed materials. The cutting performance of resin loops largely depends on the performance of the resin binder. When cutting single crystal silicon, it is required that the resin binder has good adhesion with the matrix and diamond particles to prevent diamond detachment and cutting loop failure; the friction between the resin loop and the workpiece generates a large amount of heat, necessitating good heat resistance of the resin.

Analysis of the Cutting Process

In this study, the cured hardness of four types of resin binders is tested, and their post-cured cross-sectional morphology is analyzed. Subsequently, these four resins are used to prepare diamond wire loops for cutting single crystal silicon in experiments, with an analysis of the influence of the cured hardness and post-cured density of the resin binders on cutting ability.

Summary of Experimental Results

Using four different types of phenolic resin hardness specimens and resin wire, their cured Rockwell hardness was measured. Subsequently, cutting experiments on single crystal silicon were conducted under the same cutting process to compare the relationship between Rockwell hardness and cutting performance. The following conclusions were drawn from the experiments:

（1）Phenolic resins with shorter flow length and higher curing agent content exhibit higher cured Rockwell hardness. The resin layer of the cutting wire made from this resin binder shows good adhesion to diamonds, resulting in fewer diamond particle detachments during cutting, shorter cutting times, and indicating a stronger cutting capability of the cutting wire.

（2）Phenolic resins that produce fewer small molecules during curing exhibit denser structures post-curing, with better adhesion to diamonds and stronger cutting capabilities of the cutting wire.